Member Discussion Forum

Hi,

I am after some PVB off cuts in small quantity of around 200-300 kgs. Coudl someone provide me with some contacts where I might be able to get some please. I require them to be in uncompressed form.

Thanks in advance.

Kind regards,
KG

hi,
I am learning about anticondensation on glass in buildings. I want to know the reason cause the anticondensation on glass and the clearance or solution for this problem. You can provide information for me? Thanks very much

For the glass point fixed installation ( spider system) Which type of glass is suitable? is it the Temper glass ( with Heat soaked) or just Heat Strengthened is enough?

We have a piece of 10mm tempered glass sized 1x2 meter and it was chipped about 10mm into the glass and about 1 meter along the edge. Our machine had been tested to temmpered glass to meet TUV standard. Does it mean that my glass is not fully tempered or it is the nature of tempered glass? Thanks to the experts.

I have made some solar hot water panels but am having problems with mist forming on the glass when the inside becomes hot. I am seeing a mostly dry deposit (a little greasy in areas) causing a misting. This only occurs when the temperature inside is >100 Deg C (max I have measured is 130 Deg C).

I was wondering if the problem may be agrevated by coatings on the glass, does anyone have any thoughts?

Would it be possible to remove any coatings by polishing with jewlers rouge (if it would help)?

Dear all,
we are a manufacturer of EVA film for the safety glass with over 10 years exoerienced.
The tensile breaking of the EVA film is up to 23MPA, UV resistance>99%.
If any interested, pls contact me freely. Thanks.

Hi,
Anybody knows who offers gel for manufacturing of fireproof glass?
Help! Help! Help!

Hi,

What glass I need to use for dance floor? Dance floor will be from glass segments (1,5m x 1,5m) and they will be placed on metal frame in about 20cm height. I heard that often is used 3x laminated glasses (tempered/not tempered/tempered), what thickness should they be? Also what bout clearness of this glass will be when girls with heels dance 1 year on this floor, is there will be a lot of scratches?

thanks

PS. urgent question :)

Does anyone know of the average costs associated with different methods of marking glass?-just a small logo/CE mark.
Screen printing, acid etch, sand blasting etc.

3 M is offering a tape VHB for structural glazing and avoid the silicon ……… They have the European approve for this application ?